Utjecaj dodataka novosintetiziranog organskog spoja na koroziju legure aluminija AlMg3, kositra i željeza u 3%-tnoj otopini NaCl

diplomski rad

• Naslov (engleski): The effect of the addition of a newly synthesized molecule on corrosion
• Autor: Lana Nöthig
• Mentor: Katarina Berković (mentor)
• Ustanova koja je dodijelila akademski / stručni stupanj: Sveučilište u Zagrebu; Prehrambeno-biotehnološki fakultet; (Zavod za kemiju i biokemiju); (Laboratorij za fizikalnu kemiju i koroziju); Zagreb
• Datum i država obrane: 2008-07-09, Hrvatska
• Znanstveno / umjetničko područje, polje i grana: BIOTEHNIČKE ZNANOSTI; Biotehnologija

Sažetak

U ovom radu ispitivan je utjecaj dodatka 3-hidroksi-4-hidroksiiminometil-5-hidroksimetil-2-metil-1-(4'-nitrofenacil)piridinijeva bromida na proces korozije legure aluminija (AlMg3), kositra i željeza u 3%-tnoj otopini natrijeva klorida. Vrijednosti brzina korozije uzoraka AlMg3, kositra i željeza određene su gravimetrijskom metodom promjene mase uzoraka, koji su izlagani djelovanju 3%- tne otopine NaCl kao osnovne model otopine i djelovanju 3%- tne otopine NaCl s različitim koncentracijama ispitivanog spoja (10-3, 10-4 i 10-5 mol L-1). Određivanja brzina korozije kositra i legure aluminija (AlMg3) su provedena pri temperaturama 25°C, 55°C, 70°C i 80°C, a željeza pri 25°C. Na osnovi vrijednosti brzina korozije, određene su pokrivenosti površina i stupnjevi zaštite od korozije. Ispitivani spoj pokazuje dobru zaštitu AlMg3, kositra i željeza od korozije u 3%-tnoj otopini NaCl, a učinkovitost inhibitora uglavnom raste s povećanjem koncentracije inhibitora.

Sažetak (engleski)

The effect of 3 – hydroxy – 4 hydroxyiminomethyl – 5 hydroxymethyl – 2 – methyl – 1 – (4' – nitrophenacyl) bromide on the process of corrosion of the aluminium alloy AlMg3, tin and iron in 3% saline solution was investigated. The rates of corrosion of AlMg3, tin and iron were determined by the gravimetric analysis of samples of aluminium alloys (AlMg3), tin and iron exposed to 3% NaCl solution and samples exposed concurently to 3% NaCl solution and 3–hydroxy–4 hydroxyiminomethyl – 5 hydroxymethyl –2–methyl–1–(4'–nitrophenacyl)pyridine bromide, at three different concentration levels of the investigated molecule (10-3, 10-4 and 10-5 mol L-1). The rates of corrosion of tin and iron were determined at 25°C, 55°C, 70°C and 80°C, whereas the rate of corrosion of AlMg3 was determined only at 25°C. Both the degree of surface coverage and inhibition efficiency of the investigated molecule were determined based upon the rates of corrosion of AlMg3, tin and iron in 3% NaCl solution. The investigated molecule shows efficient protection of AlMg3, tin and iron against corrosion in 3% saline solution. An increase in the concentration of the inhibitor generally results in an increase in inhibition efficiency.

• Ključne riječi: inhibitori; korozija; aluminij; kositar; željezo
• Ključne riječi (engleski): inhibitors; corrosion; aluminium alloys; tin; iron
• Jezik: hrvatski
• URN:NBN: urn:nbn:hr:159:379659
• Studijski program: Naziv: Biotehnologija; smjerovi: Biokemijsko inženjerstvo; Smjer: Biokemijsko inženjerstvo; Vrsta studija: sveučilišni; Stupanj studija: dodiplomski; Akademski / stručni naziv: diplomirani inženjer biotehnologije; smjer biokemijsko inženjerstvo (dipl. ing. bioteh.)
• Vrsta resursa: Tekst
• Način izrade datoteke: Izvorno digitalna
• Prava pristupa: Pristup korisnicima matične ustanove
• Datum i vrijeme pohrane: 2017-09-01 12:31:40