Utjecaj ekstrakata ružmarina na koroziju aluminija i aluminijske legure AlMg3 u 3% NaCl

diplomski rad

• Naslov (engleski): Influence of rosemary extracts on aluminium and aluminium alloy AlMg3 corrosion in 3% NaCl
• Autor: Andreja Čunčić
• Mentor: Katarina Berković (mentor)
• Ustanova koja je dodijelila akademski / stručni stupanj: Sveučilište u Zagrebu; Prehrambeno-biotehnološki fakultet; (Zavod za kemiju i biokemiju); (Laboratorij za fizikalnu kemiju i koroziju); Zagreb
• Datum i država obrane: 2008-03-05, Hrvatska
• Znanstveno / umjetničko područje, polje i grana: BIOTEHNIČKE ZNANOSTI; Biotehnologija

Sažetak

U ovom radu istraženo je djelovanje ekstrakata ružmarina na proces korozije aluminija i aluminijske legure AlMg3 u 3%-tnoj otopini natrijeva klorida. Određivanja su provedena gravimetrijskom metodom promjene mase i elektrokemijskom metodom potenciostatske polarizacije. Gravimetrijska određivanja brzina korozije su provedena sa tri paralelna uzorka aluminija i legure AlMg3, koji su bili izloženi djelovanju slijedećih otopina: 3% NaCl, 3% NaCl sa dodatkom otopina ružmarina pripremljenih sa vodom temperature 298,15 K i 373,15 K te 3% NaCl sa dodatkom otopina ružmarina pripremljenih s etanolom pri temperaturi 298,15 K. Određivanja struja korozije su provedena potenciostatskom metodom polarizacije legura AlMg3 u 3% NaCl i u 3% NaCl sa dodatkom otopina inhibitora. Na osnovu vrijednosti brzina korozije i struja korozije, određene su pokrivenosti površina i stupnjevi zaštite od korozije. Pripravljeni ekstrakti ružmarina su pokazali dobru zaštitu od korozije aluminija i aluminijske legure u 3%-tnoj otopini NaCl.

Sažetak (engleski)

The inhibition effect of rosemary extracts on corrosion process of aluminium and AlMg3 alloy in 3% NaCl solution has been investigated in this work. Measurements were carried out using gravimetric weight change and electrochemical potentiostatic polarization methods. Gravimetric measurements to determine corrosion rates were performed using three parallel samples of aluminium and aluminium alloy which have been immersed in following solutions: 3% NaCl, 3% NaCl containing rosemary extracts prepared with water at temperatures 298,15 K and 373,15 K and 3% NaCl containing rosemary extracts prepared with ethanol at temperature 298,15 K. Corrosion current measurements by potentiostatic polarization method were carried out on aluminium alloy AlMg3 in 3% NaCl and in 3% NaCl containing inhibitor solutions. Surface coverages and inhibition efficiensis were calculated using corrosion rate and corrosion current values. Prepared rosemary extracts have shown good protection of aluminium and AlMg3 alloy corrosion in 3% NaCl solution.

• Ključne riječi: ambalaža; korozija; inhibitori; aluminij; ružmarin
• Ključne riječi (engleski): packing; corrosion; inhibitors; aluminium; rosemary
• Jezik: hrvatski
• URN:NBN: urn:nbn:hr:159:877015
• Studijski program: Naziv: Biotehnologija; smjerovi: Biokemijsko inženjerstvo; Smjer: Biokemijsko inženjerstvo; Vrsta studija: sveučilišni; Stupanj studija: dodiplomski; Akademski / stručni naziv: diplomirani inženjer biotehnologije; smjer biokemijsko inženjerstvo (dipl. ing. bioteh.)
• Vrsta resursa: Tekst
• Način izrade datoteke: Izvorno digitalna
• Prava pristupa: Pristup korisnicima matične ustanove
• Datum i vrijeme pohrane: 2017-09-04 12:19:58